Polishing composition and polishing method using the same

ABSTRACT

A polishing composition contains an abrasive such as colloidal silica, at least one kind of compound selected from imidazole and an imidazole derivative, and water. The polishing composition preferably further contains an alkali compound, a water-soluble polymer, or a chelating agent. The polishing composition is suitable for use in polishing an edge of an object such as a semiconductor substrate.

BACKGROUND OF THE INVENTION

The present invention relates to a polishing composition for use inpolishing an edge of an object such as semiconductor substrates, and toa method for polishing an edge of an object such as semiconductorsubstrates using such a polishing composition.

Polishing compositions for use in polishing edges of semiconductorsubstrates, that is, a polishing composition for polishing edges aredisclosed in Japanese Laid-Open Patent Publications No. 11-349925 andNo. 2004-128069. In polishing of the edges of the semiconductorsubstrates, it is desired that the time required for polishing be shortand high-quality semiconductor substrates be obtained that have only asmall number of surface defects such as scratches as in polishing of thesurfaces of the semiconductor substrates. The polishing compositionsdisclosed in the above publications No. 11-349925 and No. 2004-128069have been improved to respond to such requirements. However, thepolishing composition of the above publications does not sufficientlysatisfy the requirements and there is yet room for improvements in thepolishing composition.

SUMMARY OF THE INVENTION

Accordingly, it is an objective of the present invention to provide apolishing composition more suitable for use in polishing an edge of anobject such as semiconductor substrates, and to provide a method forpolishing an edge of an object such as semiconductor substrates usingthe polishing composition.

To achieve the foregoing and other objectives and in accordance with thepurpose of the present invention, a polishing composition for use inpolishing an edge of an object is provided. The polishing compositionincludes an abrasive, at least one kind of compound selected fromimidazole and an imidazole derivative, and water.

The present invention also provides a method including polishing an edgeof an object using the above polishing composition.

The present invention also provides a method for manufacturing apolished product. The method includes: preparing the above polishingcomposition; and polishing an edge of a semi-finished product of thepolished product using the prepared polishing composition.

Other aspects and advantages of the invention will become apparent fromthe following description illustrating by way of example the principlesof the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

One embodiment of the present invention will now be described.

A polishing composition according to this embodiment contains anabrasive, imidazole or an imidazole derivative, and water.

The abrasive plays the role of mechanically polishing an object. Theabrasive preferably contains silicon dioxide, and more preferably issilicon dioxide. Silicon dioxide has superior performance in polishingthe object smoothly. Silicon dioxide may be any of colloidal silica,fumed silica, and precipitated silica, and preferably is colloidalsilica. The object polished using a polishing composition containingcolloidal silica has less surface defects such as scratches as comparedto the object polished using a polishing composition containing silicondioxide other than colloidal silica.

An abrasive having too small an average particle size is not so high inability to polish an object. In view of accelerating polishing of theobject with an abrasive, the average particle size of the abrasive inthe polishing composition obtained from the specific surface area of theabrasive measured through a BET method is preferably 10 nm or more, andmore preferably 30 nm or more, and most preferably 50 nm or more.Meanwhile, when an abrasive has too large an average particle size,there is a risk of generating scratches on the object. In view ofsuppressing formation of scratches, the average particle size of theabrasive in the polishing composition obtained from the specific surfacearea of the abrasive measured through the BET method is preferably 200nm or less, and more preferably 120 nm or less, and most preferably 80nm or less.

A polishing composition containing too small an amount of an abrasive isnot so high in polishing ability. In view of ensuring an improvement inpolishing ability of the polishing composition, the content of theabrasive in the polishing composition is preferably 0.1% by mass ormore, and more preferably 1.0% by mass or more, and most preferably10.0% by mass or more. Meanwhile, when the polishing compositioncontains a large amount of an abrasive, there is a risk of excessivelyincreasing the viscosity of the polishing composition. In view ofoptimizing the viscosity of the polishing composition, the content ofthe abrasive in the polishing composition is preferably 50.0% by mass orless.

The imidazole and the imidazole derivative in the polishing compositioncontribute to an improvement of the polishing ability of the polishingcomposition. The reason why the imidazole and the imidazole derivativecontribute to an improvement of the polishing ability is considered tobe that the unshared electron pair of the nitrogen atom at the1-position of the imidazole ring directly acts on the object.Furthermore, the imidazole and the imidazole derivative have a smallrisk of corroding the object unlike other amines such asmonoethanolamine, or 1,8-diazabicyclo(5,4,0)-undecene-7 (abbrev. DBU),and 1,5-diazabicyclo(4,3,0)-nonene-5 (abbrev. DBN).

The imidazole derivative may be one in which, for example, at least oneof hydrogen atoms bonded to the nitrogen atom at the 1-position, thecarbon atom at the 2-position, the carbon atom at the 4-position, andthe carbon atom at the 5-position of the imidazole ring is substitutedby an alkyl group such as a methyl group and an ethyl group, a hydroxygroup, a carboxy group, or an amino group.

A polishing composition containing too small an amount of imidazole oran imidazole derivative is not so high in polishing ability. In view ofensuring an improvement in polishing ability of the polishingcomposition, the content of the imidazole or the imidazole derivative inthe polishing composition is preferably 0.1% by mass or more, and morepreferably 0.5% by mass or more, and most preferably 1.0% by mass ormore. Meanwhile, when the polishing composition contains a large amountof imidazole or an imidazole derivative, there is a risk of rougheningthe surface of the polished object, since chemical corrosion of thepolishing composition becomes too strong. In view of inhibiting thesurface from roughening, the content of the imidazole or the imidazolederivative in the polishing composition is preferably 20.0% by mass orless, and more preferably 15.0% by mass or less, and most preferably10.0% by mass or less.

The water serves as a medium for dispersing or dissolving componentsother than water in the polishing composition. Water may be industrialwater, tap water, distilled water, or one obtained by filtering any ofthese, and preferably contains as little impurities as possible.

The polishing composition according to this embodiment is for use in,for example, polishing the edges of semiconductor substrates such assilicon wafers. In other words, the polishing composition is for use in,for example, polishing the edges of semi-finished products to obtainsemiconductor substrates as polished products. The edge of the object ispolished using the polishing composition, for example, by placing apolishing member such as a polishing pad in contact with the edge of theobject, and sliding either the object or the polishing member whilefeeding the polishing composition into the contact portion.

The preferred embodiment provides the following advantages.

A polishing composition according to this embodiment contains imidazoleor an imidazole derivative that contribute to an improvement ofpolishing ability of the polishing composition. Thus, the polishingcomposition of this embodiment, compared to the conventional polishingcompositions, has greater polishing ability, and promptly polishes theedge of the object, or more specifically, the edges of the semiconductorsubstrates. The polishing composition of this embodiment is hence veryuseful in polishing edges of semiconductor substrates.

The imidazole and the imidazole derivative have less risk of corrodingthe object unlike other amines such as monoethanolamine, DBU, and DBN.Therefore, the object polished using the polishing composition of thisembodiment is less corroded as compared to the object polished using thepolishing composition containing other amines such as monoethanolamine,DBU, and DBN. When a semiconductor device is manufactured from asemiconductor substrate having a large amount of corroded portion, theelectric characteristic of the semiconductor device decreases. However,the semiconductor substrate that is polished using the polishingcomposition of this embodiment is not or hardly corroded. Therefore, asemiconductor device the electric characteristic of which is suppressedfrom decreasing is manufactured from the semiconductor substrate.

When an oxidizing agent is added to the polishing composition of thisembodiment, depending on the amount of the oxidizing agent that isadded, there is a risk of forming a passivation layer on the surface ofthe object being polished. When the passivation layer is formed on thesurface of the object, there is a risk of decreasing polishing abilityof the polishing composition since polishing of the object throughchemical polishing operation of the polishing composition is hindered.However, the polishing composition of this embodiment avoids a negativeeffect caused by an oxidizing agent since the polishing composition doesnot contain the oxidizing agent.

The preferred embodiment may be modified as follows.

The polishing composition of this embodiment may further contain analkali compound. The alkali compound plays the role of chemicallypolishing an object, and contributes to an improvement of polishingability of the polishing composition. The alkali compound may containany of tetramethylammonium hydroxide, potassium hydroxide, sodiumhydroxide, potassium hydrogen carbonate, potassium carbonate, sodiumhydrogen carbonate, sodium carbonate, ammonia, ammonium hydrogencarbonate, and ammonium carbonate, and preferably includes at least onekind selected from the group consisting of tetramethylammoniumhydroxide, potassium hydroxide, and sodium hydroxide, and morepreferably includes tetramethylammonium hydroxide. Tetramethylammoniumhydroxide, potassium hydroxide, and sodium hydroxide have high abilityof polishing the object, and tetramethylammonium hydroxide hasparticularly high ability of polishing the object.

When the polishing composition contains too small an amount of an alkalicompound, the polishing ability of the polishing composition does notimprove much. In view of significantly improving polishing ability ofthe polishing composition, the content of the alkali compound in thepolishing composition is preferably 0.05% by mass or more, and morepreferably 0.25% by mass or more, and most preferably 0.5% by mass ormore. Meanwhile, when the polishing composition contains a large amountof an alkali compound, there is a risk of roughening the surface of thepolished object, since chemical corrosion of the polishing compositionbecomes too strong. In view of inhibiting the surface from roughening,the content of the alkali compound in the polishing composition ispreferably 6.0% by mass or less, and more preferably 5.0% by mass orless, and most preferably 2.0% by mass or less.

The polishing composition of this embodiment may further contain awater-soluble polymer. The water-soluble polymer acts to improve thewettability of the object. When the object has a high wettability, evenif the abrasive adheres to the object, the adhered abrasive is easilyremoved by simply washing.

The water-soluble polymer may include any of hydroxyethyl cellulose,polyvinyl alcohol, polyethylene oxide, and polyethylene glycol, andpreferably includes hydroxyethyl cellulose. Hydroxyethyl cellulose hasparticularly high ability of improving the wettability of the object.

When the water-soluble polymer has too low a molecular weight, thewettability of the polished object does not improve much. As a result,there is a risk that the abrasive in the polishing composition stronglyadheres to the object. In view of ensuring an improvement in thewettability of the polished object, the molecular weight of hydroxyethylcellulose is preferably 300,000 or more, and more preferably 600,000 ormore, and most preferably 900,000 or more. Likewise, the molecularweight of polyvinyl alcohol is preferably 1,000 or more, and morepreferably 5,000 or more, and most preferably 10,000 or more, themolecular weight of polyethylene oxide is preferably 20,000 or more, andthe molecular weight of polyethylene glycol is preferably 100 or more,and more preferably 300 or more, and most preferably 1,000 or more.Meanwhile, when the molecular weight of a water-soluble polymer isexcessively high, there is a risk of excessively increasing theviscosity of the polishing composition. In view of optimizing theviscosity of the polishing composition, the molecular weight ofhydroxyethyl cellulose is preferably 3,000,000 or less, and morepreferably 2,000,000 or less, and most preferably 1,500,000 or less.Likewise, the molecular weight of polyvinyl alcohol is preferably1,000,000 or less, and more preferably 500,000 or less, and mostpreferably 300,000 or less, the molecular weight of polyethylene oxideis preferably 50,000,000 or less, and more preferably 30,000,000 orless, and most preferably 10,000,000 or less, and the molecular weightof polyethylene glycol is preferably 20,000 or less.

When the polishing composition contains too small an amount of awater-soluble polymer, the wettability of the object does not improvemuch. In view of improving the wettability of the object, the content ofthe water-soluble polymer in the polishing composition is preferably0.0001% by mass or more, and more preferably 0.001% by mass or more, andmost preferably 0.005% by mass or more. Meanwhile, when the polishingcomposition contains a large amount of a water-soluble polymer, there isa risk of excessively increasing the viscosity of the polishingcomposition. In view of optimizing the viscosity of the polishingcomposition, the content of the water-soluble polymer in the polishingcomposition is preferably 0.5% by mass or less, and more preferably 0.3%by mass or less, and most preferably 0.15% by mass or less.

The polishing composition according to this embodiment may furthercontain a chelating agent. The chelating agent suppresses contaminationof the object with metal impurities by forming a complex ion with metalimpurities in the polishing composition thereby capturing the metalimpurities. The metal impurities in this specification refer to iron,nickel, copper, calcium, magnesium, and hydroxide or oxide of the same.

The chelating agent may be any of nitrilotriacetic acid,ethylenediaminetetraacetic acid, hydroxyethylenediaminetetraacetic acid,propanediaminetetraacetic acid, diethylenetriaminepentaacetic acid,triethylenetetraminehexaacetic acid,ethylenediaminetetraethylenephosphonic acid,ethylenediaminetetramethylenephosphonic acid,ethylenediaminetetrakismethylenephosphonic acid,diethylenetriaminepentaethylenephosphonic acid,diethylenetriaminepentamethylenephosphonic acid,triethylenetetraminehexaethylenephosphonic acid,triethylenetetraminehexamethylenephosphonic acid, andpropanediaminetetraethylenephosphonic acidpropanediaminetetramethylenephosphonic acid, and the acid of the same,which are ammonium salt, potassium salt, sodium salt, and lithium salt.

The polishing composition containing a large amount of a chelating agenteasily gelates. In view of preventing gelation, the content of thechelating agent in the polishing composition is preferably 6% by mass orless, and more preferably 3% by mass or less, and most preferably 1% bymass or less.

The polishing composition of this embodiment may contain a small amountof an oxidizing agent. When the polishing composition contains a largeamount of the oxidizing agent (for example, when the content of theoxidizing agent in the polishing composition is 1% by mass or more),there is a risk of decreasing the polishing ability of the polishingcomposition since the passivation layer is formed on the surface of theobject as described above. However, when the content of the oxidizingagent is small, the passivation layer is not formed, or only a thinpassivation layer is formed that is easily removed by mechanicalpolishing operation of the abrasive. In view of preventing reduction ofthe polishing ability of the polishing composition, the content of theoxidizing agent in the polishing composition is preferably 0.1% by massor less, and more preferably 0.01% by mass or less.

The polishing composition according to this embodiment may contain boththe imidazole and the imidazole derivative.

The polishing composition according to this embodiment may be preparedby diluting liquid concentrate with water.

The polishing composition according to this embodiment may be used forpolishing an edge of an object other than semiconductor substrates.

The present invention will now be described in more detail withreference to Examples and Comparative Examples.

In Examples 1 to 17, an abrasive, imidazole, and water were mixed, andto the mixture was added an alkali compound, a water-soluble polymer, ora chelating agent, if necessary, to prepare liquid concentrates ofpolishing compositions. In Comparative Examples 1 to 10, an abrasive andwater were mixed, and to the mixture was added imidazole or itsalternate compound, an alkali compound, a water-soluble polymer, achelating agent, or an oxidizing agent, if necessary, to prepare liquidconcentrates of polishing compositions. Types and contents of anabrasive, imidazole or its alternate compound, an alkali compound, awater-soluble polymer, a chelating agent, and an oxidizing agent in eachliquid concentrate used in Examples 1 to 17 and Comparative Examples 1to 10 are shown in Tables 1 and 2. Each liquid concentrate was dilutedwith water to ten times its volume to prepare the polishing compositionused in Examples 1 to 17 and Comparative Examples 1 to 10.

An edge of a silicon wafer was polished using each polishing compositionof Examples 1 to 17 and Comparative Examples 1 to 10 under a firstpolishing condition shown in Table 3. The difference in the weight ofeach silicon wafer before and after polishing, that is, the reducedweight of each silicon wafer was measured. The polishing rate obtainedby dividing the measured weight reduction amount of each silicon waferby polishing time is shown in the column entitled “Polishing rate” ofTables 1 and 2.

An edge of a silicon wafer was polished using each polishing compositionof Examples 1 to 17 and Comparative Examples 1 to 10 under a secondpolishing condition shown in Table 3. The edge of the polished wafer wasobserved with a microscope. Based on how much of scratches located onthe edge of the wafer before polishing has been removed, the polishingcompositions were evaluated according to a five rank scale: excellent(1), good (2), acceptable (3), slightly poor (4), and poor (5). That is,when all the scratches were removed, the polishing composition wasranked excellent; when almost all the scratches were removed, thepolishing composition was ranked good; when most of the scratches wereremoved, the polishing composition was ranked acceptable; when thescratches were not removed very much, the polishing composition wasranked slightly poor; and when the scratches were hardly removed, thepolishing composition was ranked poor. The evaluation results are shownin the column entitled “Scratches” in Tables 1 and 2.

Bare silicon wafers in chips of 32 mm×32 mm having mirror finishedsurfaces were immersed in 2.5 mass % solution of dilute hydrofluoricacid for one minute to remove a natural oxidation film formed on thesurface of each wafer. The wafers were then immersed in the polishingcompositions of Examples 1 to 17 and Comparative Examples 1 to 10. Afterone hour, the wafers were taken out of the polishing compositions andthen washed with water and dried. Subsequently, the surfaces of thewafers were visually observed. Based on how the mirror finished surfaceof the wafer has changed by chemical corrosion of the polishingcomposition, the polishing compositions were evaluated according to afive rank scale: excellent (1), good (2), acceptable (3), slightly poor(4), and poor (5). That is, when the entire surface of the wafer wasmaintained in a mirror-finished state, the polishing composition wasranked excellent; when large part of the surface of the wafer wasmaintained in a mirror-finished state, the polishing composition wasranked good; when most of the surface of the wafer is maintained in themirror-finished state, the polishing composition was ranked acceptable;when large part of the surface of the wafer was not maintained in themirror-finished state, the polishing composition was ranked slightlypoor; and when the entire surface of the wafer was not maintained in themirror-finished state, the polishing composition was ranked poor. Theevaluation results are shown in the column entitled “Corrosiveness” inTables 1 and 2. TABLE 1 Alkali Water-soluble Chelating AbrasiveImidazole compound polymer agent [mass [mass [mass [mass [mass Polishingrate percentage] percentage] percentage] percentage] percentage][mg/min.] Scratches Corrosiveness Ex. 1 colloidal silica*¹ imidazoleTMAH HEC*¹ TTHA 1.45 1 2 35.0% 4.0% 1.0% 0.008% 0.08% Ex. 2 colloidalsilica*¹ imidazole TMAH HEC*¹ TTHA 1.33 1 2 35.0% 1.0% 1.0% 0.008% 0.08%Ex. 3 colloidal silica*¹ imidazole TMAH HEC*¹ TTHA 1.62 1 2 35.0% 10.0% 1.0% 0.008% 0.08% Ex. 4 colloidal silica*¹ imidazole — — — 1.40 2 135.0% 4.0% Ex. 5 colloidal silica*¹ imidazole — HEC*¹ TTHA 1.38 1 135.0% 4.0% 0.008% 0.08% Ex. 6 colloidal silica*¹ imidazole — HEC*¹ TTHA1.24 2 1 35.0% 1.0% 0.008% 0.08% Ex. 7 colloidal silica*¹ imidazole —HEC*¹ TTHA 1.58 1 1 35.0% 10.0%  0.008% 0.08% Ex. 8 colloidal silica*¹imidazole KOH HEC*¹ TTHA 1.60 1 3 35.0% 4.0% 0.5% 0.008% 0.08% Ex. 9colloidal silica*¹ imidazole NaOH HEC*¹ TTHA 1.58 1 3 35.0% 4.0% 0.5%0.008% 0.08% Ex. 10 colloidal silica*² imidazole TMAH HEC*¹ TTHA 1.42 12 35.0% 4.0% 1.0% 0.008% 0.08% Ex. 11 colloidal silica*¹ imidazole TMAHHEC*¹ TTHA 1.15 2 2 10.0% 4.0% 1.0% 0.008% 0.08% Ex. 12 colloidalsilica*¹ imidazole TMAH HEC*¹ TTHA 1.21 2 2 20.0% 4.0% 1.0% 0.008% 0.08%Ex. 13 colloidal silica*¹ imidazole TMAH — TTHA 1.48 1 2 35.0% 4.0% 1.0%0.08% Ex. 14 colloidal silica*¹ imidazole TMAH HEC*² TTHA 1.38 1 2 35.0%4.0% 1.0% 0.008% 0.08% Ex. 15 colloidal silica*¹ imidazole TMAH HEC*³TTHA 1.46 1 2 35.0% 4.0% 1.0% 0.008% 0.08% Ex. 16 colloidal silica*¹imidazole TMAH HEC*¹ — 1.44 1 2 35.0% 4.0% 1.0% 0.008% Ex. 17 colloidalsilica*¹ imidazole TMAH HEC*¹ DTPA 1.44 1 2 35.0% 4.0% 1.0% 0.008% 0.08%

TABLE 2 Imidazole or its alternate Alkali Water-soluble ChelatingOxidizing Abrasive compound compound polymer agent agent [mass [mass[mass [mass [mass [mass Polishing rate percentage] percentage]percentage] percentage] percentage] percentage] [mg/min.] ScratchesCorrosiveness C. Ex. 1 colloidal silica*¹ — — — — — 0.48 5 1 35.0% C.Ex. 2 colloidal silica*¹ — TMAH HEC*¹ TTHA — 1.25 4 2 35.0% 2.0% 0.008%0.08% C. Ex. 3 colloidal silica*¹ — KOH HEC*¹ TTHA — 0.97 5 5 35.0% 0.5%0.008% 0.08% C. Ex. 4 colloidal silica*¹ — NaOH HEC*¹ TTHA — 1.03 5 535.0% 0.5% 0.008% 0.08% C. Ex. 5 colloidal silica*¹ — piperazine HEC*¹TTHA — 1.20 5 4 35.0% 5.0% 0.008% 0.08% C. Ex. 6 colloidal silica*¹imidazole TMAH HEC*¹ TTHA H₂O₂ 0.89 5 2 35.0% 2.5% 1.0% 0.008% 0.08%10.0% C. Ex. 7 colloidal silica*¹ DBU — HEC*¹ TTHA — 1.50 1 4 35.0% 2.5%0.008% 0.08% C. Ex. 8 colloidal silica*¹ DBU — HEC*¹ TTHA H₂O₂ 0.90 5 435.0% 2.5% 0.008% 0.08% 10.0% C. Ex. 9 colloidal silica*¹ DBN — HEC*¹TTHA — 1.46 2 4 35.0% 2.5% 0.008% 0.08% C. Ex. 10 colloidal silica*¹ DBN— HEC*¹ TTHA H₂O₂ 0.85 5 4 35.0% 2.5% 0.008% 0.08% 10.0%

TABLE 3 First Polishing condition Second Polishing condition Object tobe polished: bare silicon wafer having a Object to be polished: baresilicon wafer having a diameter of 8 inches (about 200 mm) diameter of 8inches (about 200 mm) that has Polishing machine: “EP-150/200/300-IV NF”been through tape polishing manufactured by SPEEDFAM Co., Ltd. Polishingmachine: “EP-150/200/300-IV NF” Rotation speed of drum: 1000 rpmmanufactured by SPEEDFAM Co., Ltd. Polishing load: 2.0 kgf (=approx. 20N) Rotation speed of drum: 1000 rpm Polishing pad: “DRP-II” manufacturedby Polishing load: 0.5 kgf (=approx. 5 N) SPEEDFAM Co., Ltd. Polishingpad: “DRP-II” manufactured by Inclination angle of unit: 45 degreesSPEEDFAM Co., Ltd. Vertical speed of drum: 72 mm/minute Inclinationangle of unit: 45 degrees Rotation time of lower chuck: 60 secondsVertical speed of drum: 72 mm/minute Number of polishing: 4 times(forward/backward × Rotation time of lower chuck: 60 seconds front/rear)Number of polishing: 4 times (forward/backward × Total polishing time:240 seconds front/rear) Chamfering angle: 22 degrees Total polishingtime: 240 seconds Feed rate of polishing composition: 200 Chamferingangle: 22 degrees mL/minute Feed rate of polishing composition: 200Temperature of polishing composition: 20-25° C. mL/minute Temperature ofpolishing composition: 20-25° C.

In the column entitled “Abrasive” in Tables 1 and 2, “colloidal silica*¹” represents colloidal silica having the average particle size of 55nm, which is obtained from the specific surface area measured throughthe BET method, and “colloidal silica *²” represents colloidal silicahaving the average particle size of 35 nm, which is also obtained fromthe specific surface area measured through the BET method. In the columnentitled “Alkali compound” in Tables 1 and 2, “TMAH” representstetramethylammonium hydroxide, “KOH” represents potassium hydroxide, and“NaOH” represents sodium hydroxide. In the column entitled“Water-soluble polymer” in Tables 1 and 2, “HEC *¹” representshydroxyethyl cellulose having an average molecular weight of 1,200,000,“HEC *²” represents hydroxyethyl cellulose having an average molecularweight of 300,000, and “HEC *³” represents hydroxyethyl cellulose havingan average molecular weight of 1,600,000. In the column entitled“Chelating agent” in Tables 1 and 2, “TTHA” representstriethylenetetraminehexaacetic acid, “DTPA” representsdiethylenetriaminepentaacetic acid. In the column entitled “Oxidizingagent” in Table 2, “H₂O₂” represents hydrogen peroxide.

As shown in Tables 1 and 2, the polishing rate measured using any of thepolishing compositions of Examples 1 to 17 was generally greater thanthe polishing rate measured using the polishing composition of any ofComparative Examples 1 to 10. Any of the evaluations on scratches whenusing the polishing compositions of Examples 1 to 17 was eitherexcellent or good. The results suggest that any polishing composition ofExamples 1 to 17 has high polishing ability. The polishing rate measuredusing any of the polishing compositions of Examples 1 to 3 containing analkali compound was greater than the polishing rate measured using thepolishing composition of any of Examples 5 to 7 containing no alkalicompound. The results suggest that polishing ability of a polishingcomposition is enhanced by addition of an alkali compound.

The evaluation for the corrosiveness of the polishing composition ofExample 5 containing no alkali compound is superior than the evaluationfor the corrosiveness of the polishing composition of Example 1containing tetramethylammonium hydroxide as an alkali compound.Furthermore, the evaluation for the corrosiveness of the polishingcomposition of Example 1 is superior than the evaluation for thecorrosiveness of the polishing compositions of Examples 8 and 9containing potassium hydroxide or sodium hydroxide as an alkalicompound. The results suggest that the surface roughening is caused byadding an alkali compound, and tetramethylammonium hydroxide has smallerrisk of causing surface roughening as compared to potassium hydroxideand sodium hydroxide.

1. A polishing composition for use in polishing an edge of an object,comprising: an abrasive; at least one kind of compound selected fromimidazole and an imidazole derivative; and water.
 2. The polishingcomposition according to claim 1, wherein the abrasive containscolloidal silica.
 3. The polishing composition according to claim 1,wherein the average particle size of the abrasive is 10 to 200 nm. 4.The polishing composition according to claim 1, wherein the content ofthe at least one kind of compound selected from imidazole and animidazole derivative in the polishing composition is 0.1 to 20.0% bymass.
 5. The polishing composition according to claim 1, furthercomprising an alkali compound.
 6. The polishing composition according toclaim 5, wherein the alkali compound contains at least one kind ofcompound selected from tetramethylammonium hydroxide, potassiumhydroxide, and sodium hydroxide.
 7. The polishing composition accordingto claim 1, further comprising a water-soluble polymer.
 8. The polishingcomposition according to claim 7, wherein the water-soluble polymercontains at least one kind of compound selected from hydroxyethylcellulose, polyvinyl alcohol, polyethylene oxide, and polyethyleneglycol.
 9. The polishing composition according to claim 1, furthercomprising a chelating agent.
 10. The polishing composition according toclaim 1, further comprising an oxidizing agent, wherein the content ofthe oxidizing agent in the polishing composition is less than 1% bymass.
 11. The polishing composition according to claim 1, comprising nooxidizing agent.
 12. The polishing composition according to claim 1,wherein the object is a semiconductor substrate.
 13. A method comprisingpolishing an edge of an object using a polishing composition containingan abrasive, at least one kind of compound selected from imidazole andan imidazole derivative, and water.
 14. The method according to claim13, wherein the object is a semiconductor substrate.
 15. A method formanufacturing a polished product, comprising: preparing a polishingcomposition containing an abrasive, at least one kind of compoundselected from imidazole and an imidazole derivative, and water; andpolishing an edge of a semi-finished product of the polished productusing the prepared polishing composition.
 16. The method according toclaim 15, wherein the polished product is a semiconductor substrate.